This new induction heating unit enables to translating to porosity-free dence casting, because melting
alloy is not by gas flame and never absorbs any gas. Chamber inverting casting method has no possibility
of involving oxidation film. In addition, the pressure 0.45MPa by vacuum and pressure is sufficiently
powerful compared to centrifugal casting 0.1MPa. Also,the maintaining pressure prevents shrinkage cavity
and enables to create any intricate casting results.
■ Various casting
Available at casting various cases such as Inlay, Crown, Implant framework and Denture.Usable alloy for
dental use is Precious～ Non-Precious except Titanium alloy.
■ Operation panel
The buttons are placed for the flow of casting.
|Power requirement||Single phase AC220V-240V ±10% 50/60Hz|
|Power consumption||Max. 3.5kVA|
|Environment for set up||Temp.10–40℃, Humidity 30–90%Rh (not condensing)|
|Cooling System||Optional chiller or Direct connect water|
|Melting time||Within 3 min. for 60g of Co-Cr Alloy.|
|Casting method||Chamber inverting Vacuum and Pressure Casting. (Automatic)|
|Pressure||Air or Argon gas (0.35MPa)|
|Compressed Air or Argon||Air 0.5 – 1.0MPa, Argon gas 0.5 – 0.8 MPa|
|Alloy melting quantity||Co-Cr 10-60g, Gold 10-120g but less than 10cc.|
Silver, Gold, Ceramic fused bonding alloy
(Precious, Semi-Precious, Non-Precious) except Titanium alloy
|Number of continuous casting||
Standard chiller 5-10 times depends on heating time.
Adding on Additional chiller:Available at continuous casting
Water pipe direct connecting:Available at continuous casting
|Type of crucibles||
Ceramic crucible, Carbon crucible
|Crucible inner size||
|Parameter for casting||
1 (0.5 sec.)
2 (0.7 sec.)
3 (0.9 sec.)
|Induction power at each stage (Stand by, Retention, Final) : Tuneable (0-99%)|